Damage Reasons Of magnesia Brick
Date:2015-11-24 23:15 From:Zhengzhou Sunrise Refractory Author:admin
Magnesia brick plays an important role in furnace. It can especially be mainly applied to basic open hearth furnace, steel-making furnace bottom and furnace wall, non-ferrous metal smelting furnace and high temperature tunnel kiln, especially in glass industry, magnesia brick can be used in the regenerators of glass furnace. However, mganeisa brick will be damaged when using a period, and below is the main damaged reasons analyzed by Sunrise specialist.
1. Greatly changes in Furnace temperature. There are many large fluctuations in the temperature of the furnace which makes the magnesia brick cracking. This is because the temperature suddenly changes and produces a lot of internal stress, so that the refractory brick peels, and even dumping.
2. Slag erosion. The slag intrudes into the surface of refractory brick, belonging to the physical reaction; Metal liquid or corrosive gas containing dust reacts with the surface material of refractory brick, belonging to the chemical effect. Both these two kinds of erosions will cause damage of magnesia brick.
3. Accumulation and sedimentation of gas. There is corrosive gas produced during the use of furnace, and the gas accumulates and deposits. So the damage of magnesia brick will be caused.
4. High temperature melting. Under the high temperature and heat load, the refractory brick is softened, melting, and forming the molten drop, which results in the unstability and collapse of the masonry and the refractory brick.
5. Mechanical shock. The materials in the furnace are in motion and also have physical and chemical changes at the same time. So a large mechanical impact will be produced, and the destruction is very large.
Zhengzhou Sunrise Refractory Co., Ltd. is mainly engaged in the research and development of glass refractory products. Sunrise as a glass refractory manufacturer can provide professional before-after guidance and excellent products such as fused cast AZS block, fused cast alumina block, silica brick, magnesia brick, zircon brick, zircon mullite brick, mullite series brick, sillimanite brick, etc. contact us, we will do our best for you.
1. Greatly changes in Furnace temperature. There are many large fluctuations in the temperature of the furnace which makes the magnesia brick cracking. This is because the temperature suddenly changes and produces a lot of internal stress, so that the refractory brick peels, and even dumping.
2. Slag erosion. The slag intrudes into the surface of refractory brick, belonging to the physical reaction; Metal liquid or corrosive gas containing dust reacts with the surface material of refractory brick, belonging to the chemical effect. Both these two kinds of erosions will cause damage of magnesia brick.
3. Accumulation and sedimentation of gas. There is corrosive gas produced during the use of furnace, and the gas accumulates and deposits. So the damage of magnesia brick will be caused.
4. High temperature melting. Under the high temperature and heat load, the refractory brick is softened, melting, and forming the molten drop, which results in the unstability and collapse of the masonry and the refractory brick.
5. Mechanical shock. The materials in the furnace are in motion and also have physical and chemical changes at the same time. So a large mechanical impact will be produced, and the destruction is very large.
Zhengzhou Sunrise Refractory Co., Ltd. is mainly engaged in the research and development of glass refractory products. Sunrise as a glass refractory manufacturer can provide professional before-after guidance and excellent products such as fused cast AZS block, fused cast alumina block, silica brick, magnesia brick, zircon brick, zircon mullite brick, mullite series brick, sillimanite brick, etc. contact us, we will do our best for you.